Brief Introduction of silicona RTV rubber for concrete baluster mold making
RTV-2 silicone rubber is a two component material, and it consist of Part A base silicone and Part B curing agent. When the two parts mix together and pour or brush on a object, the silicone base and curing agent can cure to be a silicone mold at room temperature; And 24 hours later, the silicone mold can be released from the object, and then the silicone mold can be poured into the following material to copy: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...
Procedures of silicona RTV rubber for concrete baluster mold making
1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
Extensive Applications of silicona RTV rubber for concrete baluster mold making
RTV-2 silicone rubber can be used in the duplication of cement molds, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.
Need more information, please feel free to contact Sophie.
| Item No. | MCSIL-2015 |
| Color | white |
| Mixing ratio | 100:2 |
| Mixed viscosity | 15500-17000 cps |
| Pot life | 30-40 Minutes |
| Curing time | 4-6 Hours |
| Hardness | 13-15 Shore A |
| Tear Strength | 25 N/mm |
| Tensile Strength | 3.8 MPA |
| Shrinkage | ≤0.3% |
| Elongation at break | 600% |
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series. We can offer all kinds of silicone rubber for your request! Any interesting, please feel free to contact us. Welcome to join us, We will always at your service.