HDPE Granulate

Virgin and recycled HDPE&LDPE&LLDPE for different grade

Specifications
1. Virgin & Recycled
2. Type: Film grade, Injection molding grade, Blowing molding grade, extrusion grade,
3. Pack: 25kg/bag
Virgin & Recycled HDPE / LDPE / LLDPE granules

We are direct factory of HDPE, LDPE, LLDPE, PP granule, different MFR or MFI are available for your different usage.

1, Film Grade HDPE,
Stretch film tape, blown film, carrier bags, film extrusion, blending partner,
Bags and density modifies, products for use in property modification

2, Fiber or Monofilament HDPE,
Monofilament, ropes, yarns

3, Injection Moulding Grade HDPE,
House wares, caps, thin walled, Transport and stacking crates, Bottle crates, Lightweight household,
Disposable articles large, Molding and complicated parts, closures/seals, packaging, Engineering parts,
Transport containers, PET bottle base cap, Injection moulding grade specially for cap

4, Below Moulding Grade HDPE,
Petro cans, containers, disinfectant bottles, sheet for thermoforming, drums, heating oil strorage tanks,
Fabric softeners, Extrusion large blow moldings, bottle extrusion

5, Pipe Extrusion Grade HDPE,
PE80, PE100, gas/water pipe, UV Stabilization and pigments during processing.

6, Extrusion Grade HDPE,
Wire&Cable

HDPE cable material Property	Unit	Typical Value
Mass density	g/cm 3	0.941-0.959
Melt flow Rate(190 centidegree /2.16kg)	g/10min	≤1.0
Tensile yield strength	MPa	≥19.0
Flexural modulus	Mpa	≥965
Elongation@ break	%	≥400
Impact Embrittlement temperature	centidegree	MAX -118
Dielectric Constant	100KHZ	2.32
	1MHZ	2.31
Loss Tangent	100KHZ	MAX 0.0001
	1MHZ	MAX 0.0001
Volume resistivity	OHM-CM	MIN 1x10 15
Application	Mainly used for the production of high toughness of the telephone,cable insulation material

 
 
LDPE:
 
 
 

Physical Properties		Test Method	Nominal Value	Unit
Density		ISO 1183	0.921	g/cm 3
Melt Mass-Flow Rate (MFR)		ISO 1133	1.9	g/10min
Hardness
Shore Hardness (shore D)		ISO 868	45
Mechanical Properties
Tensile Modulus		ISO 527-2	175	MPa
Tensile Strength	Yield,	ISO 527-2	9.0	MPa
	Break,		13.0	MPa
Tensile Strain(Break)		ISO 527-2	850	%
Modulus of Elasticity		Internal Method	250	MPa
Thermal
Vicat Softening Temperature		ISO 306/A50	89.0	°C
Melting Temperature (DSC)		DIN 53765	108	°C
Peak Crystallization Temperature (DSC)		DIN 53765	97.0	°C
Heat of Fusion		DIN 53765	110	J/g
Electrical
Volume Resistivity		ASTM D257	8.5E+15	ohm ？cm
Dielectric Strength		ASTM D149	30.0	kV/mm
Dielectric Constant (60Hz)		ASTM D150	2.20	%
Dissipation Factor (60 Hz)		ASTM D150	0.00050

 
 
 
LLDPE
 
 
 

Properties	Test conditon	Test method	Test data	Unit
Density			0.91
MFI			2
Drop impact strength		ASTM D-1709	90	g
Elongation ,vertical/horizontal		ASTM D-882	600/800	%
tensilestrength,thermal resistance		ASTM D-1004	105/95	Kg/cm
elongation		ASTM D-638	930	%
tensile strength		ASTM D-638	180
tensile strength,vertical/horizontal		ASTM D-882	380/350
Vicat softening point		ASTM D-1525	103	°C
melting point		ASTM D-2117	126	°C
Turbidity		ASTM D-1009	12	%
45 glossness		ASTM D-2457	75	%