Applications of RTV-2 Silicone for Architectural Decor Mouldings
Liquid silicon, silicones, RTV-2 silicone rubber is mainly used for Cultural relic duplication, architectural decoration, gypsum statues, Resin crafts mold making, etc.
Typical properties of RTV-2 Silicone for Architectural Decor Mouldings
Item No.: RTV 2028
Color: White
Mixing ratio 100: 2
Mixed viscosity: 30000 cps
Pot life: 30-40 mins
Curing time: 4-6 Hours
Hardness: 28-30 Shore A
Tear Strength: 30 N/mm
Tensile Strength: 4.5 Mpa
Relative density: 1.09~1.15 g/cm3
Elongation at break: 511%
How to make the silicone mold?
1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
2. Mixing Process
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35° C (95° F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.
Storage of RTV-2 Silicone for Architectural Decor Mouldings
When the silicone rubber is stored at or below 30 ° C (85 ° F) in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 10 months from the date of production. After 10 months stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series. We can offer all kinds of silicone rubber for your request! Any interesting, please feel free to contact us. Welcome to join us, We will always at your service.