Virgin & Recycled LLDPE(Linear Low-Density Polyethylene )
LLDPE granule for film/extrusion/blowing/injection grade
1. Linear Low Density Polyethlene Granules
2. Grade: Film/injection moulding/extrusion
3. Sample: Available
4. Competitive price and fast delivery
Application: Make barrela, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating.
Storage: Shelf life: It should avoid damp, contaminated and direct sun light during transport. And should be stored in ventilated and dry place. Do not put it with flammable and corrosive substances together, and away from the fire.
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
2.0±0.4 |
g/10min |
|
Density |
920±2 |
Kg/cm3 |
|
Tensile Strengthat Yield |
8 |
Mpa ≥ |
|
Tensile Strengthat Break |
12 |
Mpa ≥ |
|
haze |
15 |
%≤ |
|
Packing |
In 25 kg PP woven bags,20MT/20'FCL |
2, LLDPE for Master Batch Use
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
20 |
g/10min |
|
Density |
0.924 |
g/cm 3 |
|
Tensile Strength |
MD12 |
Mpa |
|
TD 10 |
|
Elongation at Yield |
13 |
% |
|
Elongation at Break |
200 |
|
Dark Drop Impact |
105 |
g |
|
Brittle Temperature(F 50) |
-70 |
°C |
|
Vicat Softening Point |
90 |
°C |
|
Packing |
In 25 kg PP woven bags,20MT/20'FCL |
3, LLDPE Powder Rotational Molding Grade for Tank Use
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
3.2 |
g/10min |
|
Density |
0.939 |
g/cm 3 |
|
Melting Point |
127 |
°C |
|
Tensile Yield Strength |
21 |
Mpa |
|
Tensile Strength at Break |
28 |
Mpa |
|
Elongation at Break |
1,100 |
% |
|
Flexural Modulus |
750 |
Mpa |
|
Brittle Temperature |
<-60 |
°C |
Understanding our customers, we care about the future of our business. Up to today, with reasonable price and good quality, all our products sell well in the international marketing. We want to ensure that you get our good service, only high quality and speedy delivery. We sincerely want to supply you with high quality products and perfect service based on our efficient management and professional work teams. Because professional, so trust!